Methods check details Preparation of TiO2 photoanodes TiO2 paste was blade-coated on FTO substrates and subsequently sintered at 450°C for 30 min. After cooling down to room temperature, the samples were put into 40 mmol/L TiCl4 solution at 70°C for 30 min and then sintered at 450°C for 30 min. Finally, after cooling down to 80°C, the as-prepared TiO2 photoanodes were soaked in the ethanol solution of N719 dye selleckchem for 24 h. Preparation of the counter electrodes In total,

we have prepared four kinds of CEs, including Pt/FTO, PEDOT:PSS/FTO, TiO2-PEDOT:PSS/FTO, and TiO2-PEDOT:PSS/PEDOT:PSS/glass. The Pt/FTO CE was prepared by spraying H2PtCl6 solution on the pre-cleaned FTO substrate and subsequently sintered at 450°C for 15 min. The PEDOT:PSS/FTO and TiO2-PEDOT:PSS/FTO CEs were fabricated by spin coating PEDOT:PSS (Clevios PH 1000, purchased from Heraeus, Hanau, Germany) solution and TiO2-PEDOT:PSS solution onto FTO substrates, respectively. The TiO2-PEDOT:PSS/PEDOT:PSS/glass was obtained by spin coating PEDOT:PSS mixed with 6% volume of ethylene glycol (EG) on glass substrate (5,000 rpm/s for 30 s)

and sintered at 120 °C for 15 min. This process was repeated four times. Then, the TiO2-PEDOT:PSS (40 mg P25 powder added in 1 ml PEDOT:PSS solution) solution was spin-coated on top of the PEDOT:PSS layer at 1,000 rpm/s for 40 s and sintered at 120°C for 15 min. Finally, the resultant substrates were immediately

put into EG for 30 min and then dried in the oven at 120°C for 15 min. Fabrication CX-6258 mw and characterization of DSSCs The processed TiO2 photoanodes have an active Linifanib (ABT-869) area of 0.16 cm2, and these prepared CEs were assembled together with 60-μm surlyn film, respectively. The I−/I3 − electrolyte was injected through the interspace and sealed with paraffin. The sheet resistance of the catalytic layers was measured using a four-probe tester (model RTS-8, Four Probe TECH, Guangzhou, China). The surface morphologies of CEs were scanned by field emission scanning electron microscope (quanta 200 F, FEI, OR, USA). Electrochemical impedance spectroscopy (EIS) and Tafel polarization curves were measured using an electrochemical workstation (model CHI600, CH Instruments, Inc., Austin, TX, USA) at room temperature. The current density-voltage characteristics of photocurrent density-photovoltage were simulated at AM 1.5G illumination (100 mV cm−2, XES-301S, SAN EI, Osaka, Japan) and recorded by a Keithley source meter (Keithley, Cleveland, OH, USA). Results and discussion The sheet resistance of different CEs, PEDOT:PSS/FTO CE, TiO2-PEDOT:PSS/FTO CE, TiO2-PEDOT:PSS/PEDOT:PSS/glass CE, and Pt/FTO CE, is 6.3, 7.5, 35, and 7.2 Ω sq−1, respectively.